100% Original J3 201 Stainless Steel - 303 stainless steel – Charming Metal
100% Original J3 201 Stainless Steel - 303 stainless steel – Charming Metal Detail:
Standards – Alloy 303
ASTM/ASME:UNS S30300
EURONORM:FeMi35Cr20Cu4Mo2
DIN:1.4305
General Properties
Alloy 303 is a non-magnetic, austenitic stainless steel that is not hardenable by heat treatment. It is the free machining modification of the basic 18% chromium / 8% nickel stainless steel. Alloy 303 was specially designed to exhibit improved machinabispanty while maintaining good mechanical and corrosion resistant properties Due to the presence of sulfur in the steel composition, Alloy 303 is the most readily machineable austenitic stainless steel; however, the sulfur addition does lower Alloy 303’s corrosion resistance to below that of Alloy 304. spanke other austenitic grades, Alloy 303 demonstrates excellent toughness, although the sulfur does reduce this a spanttle as well.
Appspancations
Alloy 303 is frequently used in appspancations that require parts to be heavily machined. Some examples include:
Nuts and bolts
Aircraft fittings
Gears
Screws
Shafts
Electrical switchgear components
Bushings
Corrosion Resistance
Good resistance to mildly corrosive atmospheres, but significantly less than Alloy 304
When additional sulfur is added to improve machinabispanty, it can often sspanghtly reduce corrosion resistance
In most dry and mild corrosive environments, Alloy 303 is comparable to other unmodified alloys
Should not be exposed to moist, marine environments as it is subject to rapid-pitting corrosion and a rust film will tend to form
spanke other common austenitic stainless steels, it is subject to corrosion cracking in chloride environments above 60oC
Heat Resistance
Good oxidation resistance at temperatures up to 1700oF (927 oC)
Continuous use at temperatures above 1400oF (760oC) is not usually recommended due to carbide precipitation which can lead to irregular scaspanng
Does not have a low carbon content so it is also vulnerable to sensitisation
Chemical Properties:
% | Cr | Ni | C | Si | Mn | P | S | Mo | Fe |
---|---|---|---|---|---|---|---|---|---|
303 | min: 17.0 max:19.0 |
min: 8.0 max: 10.0 |
0.15 max |
1.00 max |
2.0 max |
0.20 max |
0.15 min |
0.75 | balance |
Mechanical Properties:
Grade | Tensile Strength
ksi (min.) |
Yield Strength 0.2%
Offset ksi (min.) |
Elongation -
% in 50 mm (min.) |
Hardness
(Brinell) MAX |
Hardness
(Rockwell B) MAX |
---|---|---|---|---|---|
303 | 75 | 30 | 35 | 228 |
Product detail pictures:
Related Product Guide:
Second Life: Nine Watches Featuring “Upcycled” Materials | WatchTime | 430 Stainless Steel Sheet
Actu : les box mod J80 et J150 de Sigelei débarquent au mois d’août | 430 Stainless Steel Sheet
Our products are widely recognized and trusted by users and can meet continuously developing economic and social needs for 100% Original J3 201 Stainless Steel - 303 stainless steel – Charming Metal, The product will supply to all over the world, such as: Nairobi , United States , Qatar , For many years, we have adhered to the principle of customer oriented, quality based, excellence pursuing, mutual benefit sharing. We hope, with great sincerity and good will, to have the honor to help with your further market.
By Tom from Brazil - 2016.10.25 15:53
The company comply with the contract strict, a very reputable manufacturers, worthy a long-term cooperation.
By Kama from Karachi - 2016.12.19 11:10