409, 409L, 410,410S, 430 coil azzar inossidabbli
ħxuna | 0.15mm-2.0mm |
tolleranza ħxuna | +/- 0.02mm |
wisa | 600mm '1250mm |
tolleranza wisa | +/- 2mm |
kisja taż-żingu | Z40-Z275 AZ30-AZ150 |
kulur | Griż, baħar abjad blu, aħmar jew kwalunkwe standard RAL |
pittura | Top: 20 + -5um Dahar: 5μm-8μm |
standard | ASTM, AISI, DIN, GB, JIS |
materjal | SGCC, SGCD, SECC, SECD, DX51D + Z, S350GD, S450GD, S550GD |
teknika | Cold rolled, hot dipped iggalvanizzar, kulur miksi, galvanizzat, galvalume |
spangle | Żero spangle, spangle regolari jew spangle normali |
wiċċ Struttura | Galvanizzat, galvalume, spangle żero, spangle regolari jew spangle normali |
trattament tal-wiċċ | Kromat u oiled, kromat u mhux oiled |
ippakkjar | istandard esportazzjoni, jew skond il-ħtieġa tal-klijent |
ordni min | 500 tunnellata |
piż kolja | 3-6tons jew bħala ħtieġa tal-klijent. |
coil ID | 508 / 610mm
|
Kompożizzjoni kimika
grad | C | si | Mn | P≤ | S≤ | cr | mo | ni | oħra |
409 | ≤0.03 | ≤1.00 | ≤1.00 | 0.04 | 0.03 | 10.5-11.7 | - | ≤0.6 | Ti = 6 × C% ~ 0.75 |
410 | ≤0.15 | ≤1.00 | ≤1.00 | 0.04 | 0.03 | 11.5-13.5 | - | - | - |
410S | ≤0.08 | ≤1.00 | ≤1.00 | 0.04 | 0.03 | 11.5-13.5 | - | - | - |
420 | ≤0.15 | ≤1.00 | ≤1.00 | 0.04 | 0.03 | 12.0-14.0 | - | - | - |
430 | ≤0.12 | ≤0.75 | ≤1.00 | 0.04 | 0.03 | 16-18 | - | ≤0.4 | - |
Proprjetajiet mekkaniċi
grad | YS (MPa) ≥ | TS (MPa) ≥ | El (%) ≥ | Ebusija (HV) ≤ |
409 | 175 | 360 | 20 | 150 |
410 | 200 | 440 | 20 | 145 |
410S | 200 | 410 | 20 | 145 |
430 | 200 | 450 | 25 | 145 |
grad | applikazzjoni |
409 | Karozzi pajp, silencer |
410 | Flat molol, skieken, utensili tal-kċina u għodda tal-idejn |
420 | Qtugħ għodda, kejl għodda, strumenti dentali u kirurġiċi, xaftijiet pompa, forom tal-plastik u tmut, blalen azzar, imqassijiet, xaftijiet gear, cams, jagħmel pern, forom Lens |
430 | Sinkijiet, sink rimmijiet, apparat raqam, uċuħ kontro, woxers dixx, barnużi firxa, platti, użi arkitettoniku, soqfa, Binarju żgħir u tagħmir tar-ristoranti. |