301, 304, 304L, 316, 316L, 309 S, 310, 321 STAINLESS Stolindustrie verhënnert
Spezifizéierung
Schouljoer | 301, 304, 304L, 316, 316L, 309 S, 310, 321 |
Standard | ASTM A240, JIS G4304, G4305, GB / T 4237, GB / T 8165, BS 1449, DIN17460, DIN 17441 |
Duerchmiesser | Als Clienten Noutwendegkeete |
Längt | 1000mm-8000mm oder als Clienten 'Ufro |
Uewerfläch virum | NO1, No.4,2B, BA, 6K, 8K, Hair Linn mat PVC |
chemescher Zesummesetzung
Schouljoer | C | si | biergof | P≤ | S≤ | CR | mo | Ni | aner |
301 | ≤0.15 | ≤1.00 | ≤2.00 | 0,045 | 0,03 | 16-18 | - | 6.0 | - |
304 | ≤0.07 | ≤1.00 | ≤2.00 | 0,035 | 0,03 | 17-19 | - | 8.0 | - |
304L | ≤0.075 | ≤1.00 | ≤2.00 | 0,045 | 0,03 | 17-19 | - | 8.0 | ? |
309S | ≤0.08 | ≤1.00 | ≤2.00 | 0,045 | 0,03 | 22-24 | - | 12,0 | - |
310 | ≤0.08 | ≤1.5 | ≤2.00 | 0,045 | 0,03 | 24-26 | - | 19,0 | - |
316 | ≤0.08 | ≤1.00 | ≤2.00 | 0,045 | 0,03 | 16-18.5 | 2 | 10.0 | - |
316L | ≤0.03 | ≤1.00 | ≤2.00 | 0,045 | 0,03 | 16-18 | 2 | 10.0 | - |
321 | ≤0.12 | ≤1.00 | ≤2.00 | 0,045 | 0,03 | 17-19 | - | 9.0 | Ti≥5 × C |
Schouljoer | Sten (Mpa) ≥ | TS (Mpa) ≥ | El (%) ≥ | Hardness (HV) ≤ |
301 | 200 | 520 | 40 | 180 |
304 | 200 | 520 | 50 | 165-175 |
304L | 175 | 480 | 50 | 180 |
309S | 200 | 520 | 40 | 180 |
310 | 200 | 520 | 40 | 180 |
316 | 200 | 520 | 50 | 180 |
316L | 200 | 480 | 50 | 180 |
321 | 200 | 520 | 40 | 180 |
?
?
?
?
?
Applikatioun
- Raumfaarttechnik
- Metal Service Centren
- nuklear
- Marine / Shipbuilding
- chemesche Processing
- Ueleg & Gas
- Liewensmëttel Service / Restaurant
- nei Ierfgroussherzogin
- Regierung / Military
- Pompelen & Jesuskand
- Machined fabrizéierte Komponenten
- Power Distribution
- Fabricator