301, 304, 304L, 316, 316L, 309 S, 310, 321 ba asye pur
Spesifikasyon
Klas | 301,304,304L,316,316L,309 S,310,321 |
Estanda | ASTM A240, JIS G4304, G4305, GB/T 4237, GB/T 8165, BS 1449, DIN17460, DIN 17441 |
Dyamèt | Kòm kondisyon kliyan yo |
Longè | 1000mm-8000mm oswa kòm demann kliyan yo |
Sifas fini | NO1, No.4,2B, BA, 6K, 8K, Liy cheve ak PVC |
Konpozisyon chimik
Klas | C | Si | Mn | P≤ | S≤ | Cr | Mo | Ni | Lòt |
301 | ≤0.15 | ≤1.00 | ≤2.00 | 0.045 | 0.03 | 16-18 | - | 6.0 | - |
304 | ≤0.07 | ≤1.00 | ≤2.00 | 0.035 | 0.03 | 17-19 | - | 8.0 | - |
304L | ≤0.075 | ≤1.00 | ≤2.00 | 0.045 | 0.03 | 17-19 | - | 8.0 | ? |
309S | ≤0.08 | ≤1.00 | ≤2.00 | 0.045 | 0.03 | 22-24 | - | 12.0 | - |
310 | ≤0.08 | ≤1.5 | ≤2.00 | 0.045 | 0.03 | 24-26 | - | 19.0 | - |
316 | ≤0.08 | ≤1.00 | ≤2.00 | 0.045 | 0.03 | 16-18.5 | 2 | 10.0 | - |
316L | ≤0.03 | ≤1.00 | ≤2.00 | 0.045 | 0.03 | 16-18 | 2 | 10.0 | - |
321 | ≤0.12 | ≤1.00 | ≤2.00 | 0.045 | 0.03 | 17-19 | - | 9.0 | Ti≥5×C |
Klas | YS(Mpa) ≥ | TS (Mpa) ≥ | El (%) ≥ | Dite (HV) ≤ |
301 | 200 | 520 | 40 | 180 |
304 | 200 | 520 | 50 | 165-175 |
304L | 175 | 480 | 50 | 180 |
309S | 200 | 520 | 40 | 180 |
310 | 200 | 520 | 40 | 180 |
316 | 200 | 520 | 50 | 180 |
316L | 200 | 480 | 50 | 180 |
321 | 200 | 520 | 40 | 180 |
?
?
?
?
?
Aplikasyon
- Aerospace
- Sant sèvis metal yo
- Nikleyè
- Marin/Konstriksyon bato
- Pwosesis chimik
- Lwil oliv ak gaz
- Sèvis Manje/Restoran
- Motorsports
- Gouvènman/Milite
- Ponp & Tiyo
- Machin fabrike konpozan
- Distribisyon pouvwa
- Faktori