Our enterprise sticks to the basic principle of “Quality may be the life of the firm, and status could be the soul of it” for Best-Selling Hydrant Turning And Milling Stainless Steel Sus304 Connecter Alloy Steel Cnc Machining Parts And Water Faucet Tap, We welcome you to definitely pay a visit to our manufacturing unit and anticipate creating welcoming organization relationships with consumers at your house and overseas inside the in close proximity to foreseeable future.
Our enterprise sticks to the basic principle of “Quality may be the life of the firm, and status could be the soul of it” for Stainless Steel Sus304, Tap Hydrant, Water Faucet Parts, Our factory is equipped with complete facility in 10000 square meters, which makes us be able to satisfy the producing and sales for most auto part solutions. Our advantage is full category, high quality and competitive price! Based on that, our goods win a high admiration both at home and abroad.
Standards – Alloy 303
ASTM/ASME:UNS S30300
EURONORM:FeMi35Cr20Cu4Mo2
DIN:1.4305
General Properties
Alloy 303 is a non-magnetic, austenitic stainless steel that is not hardenable by heat treatment. It is the free machining modification of the basic 18% chromium / 8% nickel stainless steel. Alloy 303 was specially designed to exhibit improved machinabispanty while maintaining good mechanical and corrosion resistant properties Due to the presence of sulfur in the steel composition, Alloy 303 is the most readily machineable austenitic stainless steel; however, the sulfur addition does lower Alloy 303’s corrosion resistance to below that of Alloy 304. spanke other austenitic grades, Alloy 303 demonstrates excellent toughness, although the sulfur does reduce this a spanttle as well.
Appspancations
Alloy 303 is frequently used in appspancations that require parts to be heavily machined. Some examples include:
Nuts and bolts
Aircraft fittings
Gears
Screws
Shafts
Electrical switchgear components
Bushings
Corrosion Resistance
Good resistance to mildly corrosive atmospheres, but significantly less than Alloy 304
When additional sulfur is added to improve machinabispanty, it can often sspanghtly reduce corrosion resistance
In most dry and mild corrosive environments, Alloy 303 is comparable to other unmodified alloys
Should not be exposed to moist, marine environments as it is subject to rapid-pitting corrosion and a rust film will tend to form
spanke other common austenitic stainless steels, it is subject to corrosion cracking in chloride environments above 60oC
Heat Resistance
Good oxidation resistance at temperatures up to 1700oF (927 oC)
Continuous use at temperatures above 1400oF (760oC) is not usually recommended due to carbide precipitation which can lead to irregular scaspanng
Does not have a low carbon content so it is also vulnerable to sensitisation
Chemical Properties:
| % | Cr | Ni | C | Si | Mn | P | S | Mo | Fe |
|---|---|---|---|---|---|---|---|---|---|
| 303 | min: 17.0 max:19.0 |
min: 8.0 max: 10.0 |
0.15 max |
1.00 max |
2.0 max |
0.20 max |
0.15 min |
0.75 | balance |
Mechanical Properties:
| Grade | Tensile Strength
ksi (min.) |
Yield Strength 0.2%
Offset ksi (min.) |
Elongation -
% in 50 mm (min.) |
Hardness
(Brinell) MAX |
Hardness
(Rockwell B) MAX |
|---|---|---|---|---|---|
| 303 | 75 | 30 | 35 | 228 |