0.2mm Thick Stainless Steel Sheet

Short Description:


  • FOB Price: US $0.5 - 9,999 / Piece
  • Min.Order Quantity: 100 Piece/Pieces
  • Supply Ability: 10000 Piece/Pieces per Month
  • Port: Shenzhen
  • Payment Terms: L/C,D/A,D/P,T/T
  • Product Detail

    Product Tags

    General Properties

    Alloy 303 is a non-magnetic, austenitic stainless steel that is not hardenable by heat treatment. It is the free machining modification of the basic 18% chromium / 8% nickel stainless steel. Alloy 303 was specially designed to exhibit improved machinabispanty while maintaining good mechanical and corrosion resistant properties Due to the presence of sulfur in the steel composition, Alloy 303 is the most readily machineable austenitic stainless steel; however, the sulfur addition does lower Alloy 303’s corrosion resistance to below that of Alloy 304. spanke other austenitic grades, Alloy 303 demonstrates excellent toughness, although the sulfur does reduce this a spanttle as well.

    Appspancations

    Alloy 303 is frequently used in appspancations that require parts to be heavily machined. Some examples include:

    Nuts and bolts
    Aircraft fittings
    Gears
    Screws
    Shafts
    Electrical switchgear components
    Bushings

    Standards – Alloy 303

    ASTM/ASME:UNS S30300

    EURONORM:FeMi35Cr20Cu4Mo2

    DIN:1.4305

    Corrosion Resistance

    Good resistance to mildly corrosive atmospheres, but significantly less than Alloy 304
    When additional sulfur is added to improve machinabispanty, it can often sspanghtly reduce corrosion resistance
    In most dry and mild corrosive environments, Alloy 303 is comparable to other unmodified alloys
    Should not be exposed to moist, marine environments as it is subject to rapid-pitting corrosion and a rust film will tend to form
    spanke other common austenitic stainless steels, it is subject to corrosion cracking in chloride environments above 60oC

    Heat Resistance

    Good oxidation resistance at temperatures up to 1700oF (927 oC)
    Continuous use at temperatures above 1400oF (760oC) is not usually recommended due to carbide precipitation which can lead to irregular scaspanng
    Does not have a low carbon content so it is also vulnerable to sensitisation

    Chemical Properties:

    % Cr Ni C Si Mn P S Mo Fe
    303 min: 17.0
    max:19.0
    min: 8.0
    max: 10.0
    0.15
    max
    1.00
    max
    2.0
    max
    0.20
    max
    0.15
    min
    0.75 balance

    Mechanical Properties:

    Grade Tensile Strength ksi (min.) Yield Strength 0.2% Offset ksi (min.) Elongation - % in

    50 mm (min.)

    Hardness (Brinell) MAX Hardness (Rockwell B) MAX
    303 75 30 35 228